Density before sintering (g/cm3) : 3.1±0.5 g/cm3
CTE after sintering (25-200℃) : 6.08±0.01 g/cm3
3-point bending strength after sintering (MPa) : 1100Mpa
Chemical solubility after sintering (μg/cm2) : < 15%
Cytotoxicity test : < 100
Sintering temperature (℃) : 1450-1550℃Recommended 1530℃
ST Multilayer Yttria Stabilized Zirconia Ceramic for Wieland System
The blanks, which are homogeneously shaded in an industrial process, can be sintered immediately after milling and make the work process efficient and process reliable. As they are available in 4 shade gradations, the user gains from economic fabrication with a high degree of shade stability and aesthetics.
We choose the best zirconia powder and utilize a cold isostatic pressing system to form shapes;
the main advantage of isostatic pressing is the uniform application of pressure, which leads to
a very homogeneous density and shrinkage, yielding a very reproducible process. The
production cost by using isostatic pressing is much higher than uniaxel dry pressing,
but quality is also much higher. We try to provide high quality, low cost zirconia blocks
for all dental CAD/CAM milling system, support open architecture CAD/CAM milling
system.
Specifications
Wieland System |
D98*10 |
D98*12 |
D98*14 |
D98*16 |
D98*18 |
D98*20 |
D98*22 |
D98*25 |
| ST -Multilayer |
crown | √ |
Bridge | √ |
3-4 units bridge | √ |
5-6 units bridge | √ |
Bridges over 7 units | √ |
Cantilever bridge | √ |
Inlay bridge | √ |
Maryland bridge | √ |
Telescopic crown | √ |
Personalized abutment | √ |
ST Multilayer Yttria Stabilized Zirconia Ceramic For Wieland System Images |
Friendly Links: www.everychina.com
Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们